亞克力板化學(xué)性能表
25℃時(shí)在試劑中浸泡7天后增重，%
Wt.%gained after 7 days immersion at 25℃
試劑
?Reagent | 濃度
?Concentretion | 增重%
?Weight Gain% | 外觀變化
?Change in Appearence |
Hydrochloric acid | 鹽酸 | 10% | 0.30 | None | 不變 |
Hydrochloric acid | 鹽酸 | 比重1.19 | -0.04 | None | 不變 |
Nitric acid | 硝酸 | 40% | 9.7 | None | 不變 |
Nitric acid | 硝酸 | 比重1.42 |
| Dissolved | 被溶解 |
Sulfuric acid | 硫酸 | 30% | 0.19 | None | 不變 |
Sulfuric acid | 硫酸 | 比重1.80 |
| Swollen and dissolved | 溶脹并溶解 |
Hydrochloric acid | 氫氟酸 | 40% | 20.4 | Swollen | 溶脹 |
Acetic acid | 醋酸 | 5% | 0.44 | None | 不變 |
Acetic acid | 醋酸 | 比重1.05 |
| Dissolved | 被溶解 |
Citric acid | 檸檬酸 | 10% | 0.46 | None | 不變 |
Hydrogen Peroxide | 雙氧水 | 28% | 0.68 | None | 不變 |
Oleic acid | 油酸 |
| -0.25 | None | 不變 |
Chromic acid | 鉻酸 | 40% | 0.23 | None | 不變 |
Ammonium hydroxide | 氨水 | 10% | 0.36 | None | 不變 |
Ammonium hydroxide | 氨水 | 比重0.9 | 0.33 | None | 不變 |
Sodium hydroxide | 氫氧化鈉 | 10% | 0.31 | None | 不變 |
Sodium hydroxide | 氫氧化鈉 | 50% | -0.42 | None | 不變 |
Sodium Chloride | 氯化鈉 | 10% | 0.39 | None | 不變 |
Sodium Carbonate | 碳酸鈉 | 20% | 0.33 | None | 不變 |
Acetone | 丙酮 |
|
| Dissolved | 被溶解 |
Aniline | 苯胺 |
|
| Dissolved | 被溶解 |
Ethyl | 乙醇 | 95% | 0.07 | None | 不變 |
alcohol | 苯 |
|
| Dissolved | 被溶解 |
Benzene | 四氧化碳 |
|
| Cracked | 開裂 |
Carbon tetrachloride | 二乙醚 |
| 0.2 | None | 不變 |
Diethyl formemide | 二甲替甲酰胺 |
|
| Dissolved | 被溶解 |
Ethyl acetate | 乙酸乙酯 |
|
| Dissolved | 被溶解 |
Ethylene dichloride | 二氯乙烯 |
|
| Dissolved | 被溶解 |
n-heptane | 正庚烷 |
| -0.03 | None | 不變 |
iso0Octane | 異辛烷 |
| -0.03 | None | 不變 |
Kerosens | 煤油 |
| 0.01 | None | 不變 |
Toluene | 甲苯 |
|
| Crazing | 裂紋 |
Mineral oil | 礦物油 |
| 0.03 | None | 不變 |
olive oil | 橄欖油 |
| 0.19 | None | 不變 |
Transformer oil | 變壓器油 |
| 0.04 | None | 不變 |
Turpentine | 松節(jié)油 |
| 0.15 | None | 不變 |
Water(distilled) | 蒸餾水 |
| 0.43 | None | 不變 |
Phenolio solution | 苯酚溶液 | 5% | 3.6 | Swollen slightly | 輕微溶脹 |
Cotton oil | 棉花油 |
| -0.26 | None | 不變 |
Detergent solution | 清潔劑溶液 |
| 0.48 | None | 不變 |
Lacquer thinner | 油漆稀釋劑 |
|
| Dissolved | 被溶解 |
?
?